This depends on what kind of temperature and strain rates you are talking about, and what material. If you mean 70f VS 80f, then you won't be able to tell a difference for most metals. If you mean 70f VS 800f then yes there will be a difference. A one hour test VS a two hour test is probably not much different. A one hour test VS a 1 millisecond test will be ...